This study evaluated the efficacy of Endosolv-R and Xylene in softening epoxy resin based sealer after 1 to 2 min exposure.

Sixty Teflon molds (6 mm × 1.5 mm in inner diameter and depth) were equally divided into 3 groups of 20 each. AH 26 (Dentsply/De Trey), AH Plus (Dentsply/De Trey), Adseal (Meta-Biomed) were manipulated and placed in the molds allotted to each group and allowed to set at 37℃ in 100% humidity for 2 wk. Each group was further divided into 2 subgroups according to the solvents used, i.e. Xylene (Lobachemie) and Endosolv-R (Septodont). Specimens in each subgroup were exposed to respective solvents for 1 and 2 min and the corresponding Vicker's microhardness (HV) was assessed. Data was analysed by Mauchly's test and two-way analysis of variance (ANOVA) with repeated measures, and one-way ANOVA.

Initial hardness was significantly different among the three sealers with AH Plus having the greatest and Adseal having the least. After 2 min, Xylene softened AH Plus and Adseal sealer to 11% and 25% of their initial microhardness, respectively (p < 0.001), whereas AH 26 was least affected, maintaining 89.4% of its initial microhardness. After 2 min, Endosolv-R softened AH 26, AH Plus and Adseal to 12.7, 5.6 and 8.1% of their initial microhardness, respectively (p < 0.001).

Endosolv-R was a significantly more effective short term softener for all the tested sealers after 2 min whereas Xylene was an effective short term softener against AH plus and Adseal but less effective against AH 26.

The purpose of this study was to evaluate curing degree of three dual-cure resin cements with the elapsed time in self-cure and dual-cure mode by means of the repeated measure of micro-hardness.

Two dual-cure self-adhesive resin cements studied were Maxcem Elite (Kerr), Rely-X Unicem (3M ESPE) and one conventional dual-cure resin cement was Rely-X ARC resin cement (3M ESPE). Twenty specimens for each cements were made in Teflon mould and divided equally by self-cure and dual-cure mode and left in dark, 36℃, 100% relative humidity conditional-micro-hardness was measured at 10 min, 30 min, 1 hr, 3 hr, 6 hr, 12 hr and 24 hr after baseline. The results of micro-hardness value were statistically analyzed using independent samples t-test and one-way ANOVA with multiple comparisons using Scheffe's test.

The micro-hardness values were increased with time in every test groups. Dual-cure mode obtained higher micro-hardness value than self-cure mode except after one hour of Maxcem. Self-cured Rely-X Unicem showed lowest value and dual-cured Rely-X Unicem showed highest value in every measuring time.

Sufficient light curing to dual-cure resin cements should provided for achieve maximum curing.