- Original Article Surface roughness and color stability of various composite resins
- Sung-Yi Lee, Hyeon-Cheol Kim, Bock Hur, Jeong-Kil Park
-
2007;32(6):-549.
DOI: https://doi.org/10.5395/JKACD.2007.32.6.542
Published online: November 30, 2007
Department of Conservative Dentistry, School of Dentistry, Pusan National University, Busan, Korea. JFIF d d Ducky d qhttp://ns.adobe.com/xap/1.0/ |er˭|I|-fGK.rΛp8XV1%K6mvG+tc+qE &ǸC_Nm:l=_/m5^[dߌڇ.c<%:)tQ$Ow~-aY;UJ >=F)2[nk؆?훐 M=l6[4(O.]2#-H^n#->&mp5~Fӛ+|| S,xag% qkEUzUgæBhߕP(7]kFnq?֖Cpru Z6*rEڊtS|*tI*E}7R<,nUU֫^I7Q*mSly%rdȓd8hE<9oHhMfNSRj[i7D[Rj݊+kდq{"$$H?p \̅S?㭻;t~ R߁ )^/>Qj`yt[w ԛ;² ~+ ߔ_ YW~|o] ?x^ᯛ `ʼn;g)T@vWn]>&4l p+$D̢1l|ȨF%-} .9[}w~
ԠLM9hСablfe&QoW !s ?wjLK?s7yO>(=C~_nyǜu? v 3vyo oI@qV-jeES^[9WoSܝh"l2C1a͔CiJ@3:Pճw= /7ovuk+\V;lDgն <[A+r X~d;m!_s8ݖ;;.0llUC+?i#_crʙ1~C.\q u l8Hܶ2m`ܻM3Tov|Bs rɵ"oLS-
DКw=Tv@f '6|YlD͓Y%-#Ѯo%:&!3o%\J<02;K87>^vgƓ# ;ݝmz^Y6=PS39U%~
&f#
}o!muH; ʲŇ˷yvP+&.7e[3'vR4Yj̗IZ`e˽3o[WU{
m[sUbۋZǾۆl6~9'V*.\S2<Sd*zY[aŶ`]C$n.v^Ʌ
dng>ەZ,Mmϑ :n6nϦezW qUJ4! ۇ4R! =>>F n|Q[{pRO 17ƕ~._I ''00k=b՛o}Osðc2'o\3}ݭQ^ 2 . R1yKȣtAݿ-u ܾw!`?1Whn|gzU o[ECWwjUIן)^h#1ɭ!/Z
np;o;ΗŻkXs."6E`Z1
עӐ9Kl8qd q} 2Stt;#j>;խabONŗ=fwP1j)l6J̶|gV 2`y/0E˛6+ԫ1?
6}KW c\KoKͨ2ۅFws*TԞLיuDx .kCzWXhy۶gLu|%TnupǺl-S* P RaLnT+c+*xl.v!.U=|; !_L̎뱚U=4hm:ٯ"y)$:>%(n}X'p[ȴ
^˒4kƓmzDx
\
'Nq amP7nyN݅=
- Corresponding Author: Jeong-Kil Park. Department of Conservative Dentistry, School of Dentistry, Pusan National University, 1-10, Ami-dong, Seo-gu, Busan, 602-739, Korea. Tel: 82-51-240-7456, jeongkil@pusan.ac.kr
• Received: September 16, 2007 • Revised: November 12, 2007 • Accepted: November 13, 2007
Copyright © 2007 Korean Academy of Conservative Dentistry
- 1,849 Views
- 8 Download
- 8 Crossref
Abstract
- The purpose of this study was to evaluate the difference in the surface roughness after polishing and to evaluate the difference in color stability after immersion in a dye solution among four types of composite resin materials. Four light-polymerized composite resins (Shade A2) with different sized filler content (a nanofilled, a hybrid, a microfilled, a flowble) were used. Average surface roughness (Ra) was measured with a surface roughness tester (Surftest Formtracer) before and after polishing with aluminum oxide abrasive discs (Super-Snap). Color of specimens before and after staining with 2% methylene blue solution were measured using spectrophotometer (CM-3700d) with SCI geometries. The results of Ra and ΔE were analyzed by one-way analysis of variance (ANOVA), a Scheffe multiple comparison test and Student t-test (p = 0.05). After polishing, Ra values were decreased regardless of type of composite resins. In surface roughness after polishing and color stability after staining, nanofilled composite resin was not different with other composite resins except flowable resins.
I. INTRODUCTION
The smooth surface of a restoration provides both optimum esthetics and longevity1). Surface irregularities may create clinical problems such as staining, plaque accumulation, recurrent caries and periodontal disease2,3). Also rough surface of composite resin restorations results in staining and discoloration due to infiltration of colorants4). It decreases color stability, replacement of restoration should be required. In addition, rough surfaces would influence a dispersion of the light and reflection degree and affect the hue or the translucency of the surface. Though the color change of rough surface is not visible, it has an influence on optical properties. Replacement of restoration or additional polishing would be needed from unesthetic appearance5). Therefore, making smooth surface of composite resin restorations is essential step in restorative dentistry6).
Surface roughness of composite resins is basically influenced by (1) the size, hardness, and amount of filler, (2) resin matrix composition, (3) hardness and grit size of the abrasives during polishing7-9). Among these various factors, character istics of filler particle such as size and volume should be regarded as one of the important factors. The increase of the filler contents and the reduction of the filler size contributed to reduce the wear rates10-12) and to improve the surface smoothness of composite resin restorations10,13,14).
It was reported that larger filler-particle size resulted in rougher surfaces1,16). There are many composite resins have various filler size and volume. In the last decades, the size of the filler particles in dental resin composite materials has decreased considerably, from 8-30 µm in traditional composites to 0.7 - 3.6 µm for modern small-particle composites15). The use of composite resins with a higher small-sized filler-particle content is increasing17). Increased amount of filler contents, decreased filler size and better distribution within the resin matrix result in smoother surfaces9).
Recently, nanotechnology is of great interest in resin composite research. Nanofilled materials are contain nanometric particles and nanoclusters in a conventional resin matrix18). Nanofilled materials are believed to offer excellent wear resistance, strength and ultimate esthetics due to their exceptional polishability, polish retention and lustrous appearance19). And, the small size of the filler particles improves the optical properties of resin composites. The human's eye cannot detect the filler particles, because their diameter is lower than the wavelength of visible light (0.4 - 0.8 µm). As improving physical and optical properties, manufacturers now recommend the use of nanocomposites for both anterior and posterior restorations.
The aesthetics of restoration is influenced by the color stability of composite resin restorations as well as smooth surfaces. Discoloration of tooth-colored, resin-based materials may be caused by intrinsic and extrinsic factors20). The intrinsic factors involve the discoloration of the resin material itself, such as the alteration of the resin matrix and of the interface of matrix and fillers20). Extrinsic factors for discoloration include staining by adsorption or absorption of colorants as a result of contamination from exogenous sources such as coffee, tea, and beverages21-23). Extrinsic factors include mechanical wear, microleakage, incomplete adhesion of composite resins and teeth, and rough surface24-27). Barkmeier and Cooley28) were reported that the rougher of composite resin surface, the higher chance of staining and discoloration. Therefore, color stability of esthetic dental materials should also be important for a successful restoration with composite resins.
Among the numerous parameters, surface roughness and color change measurement are generally performed procedure and they are convenient for comparison of surface condition of composite resin restorations. Color change mathematically expresses the amount of difference between the L*a*b* coordinates of different specimens or the same specimen at different instances29). The Commission Internationale de l' Eclairage (CIE) L*a*b* color system, which is related to the color perception of the human eye for 3 coordinates, is an approximately uniform color space with coordinates for lightness, namely white-black (L*), red-green (a*), and yellow-blue (b*)30). A spectrophotometer with an integrating sphere can operate at two different measuring geometries the specular component included (SCI) geometry, and the specular component excluded (SCE) geometry31).
The objectives of this study were to evaluate the difference in the surface roughness among 4 types of composite resin materials before and after polishing and to evaluate the difference in color stability on color measuring geometries of SCE after immersion in a dye solution among four types of composite resin materials.
II. MATERIALS AND METHODS
In this study, four light-polymerized composite resins (Shade A2) with different sized filler contents were used (Table 1). All the resin composites were packed into a teflon mold (8 mm in diameter and 2 mm in thickness) on a cover glass. After packing the composites, light cured for 30 seconds with a light-curing unit (Bluephase, Ivoclar vivadent, Shann, Liechte-nstein) with an output of 610 mW/cm2. Ten specimens were prepared for each composite. All specimens were finished with green stone and white stone.
The Ra of ten specimens of each composite measured with a cutoff value of 0.8 mm, a measuring speed of 0.5 mm/s with a surface roughness tester (Surftest Formtracer, Mitutoyo, Kanagawa, Japan). After then, the specimens were polished sequentially with medium, fine and superfine aluminum oxide abrasive discs (Super-Snap, Shofu, Kyoto, Japan) for 30 seconds. After polishing, the Ra of ten specimens of each composite measured.
In sequence, staining procedure was performed. Each specimen was immersed separately into 2% methylene blue solution for 24h. After immersion, specimens were rinsed with distilled water for 30 seconds.
Measurement was made between before and after polishing and after staining, according to CIE L*a*b* color scale relative to the CIE standard illuminant D65 over a white background on reflection spectrophotometer (CM-3600d, Minolta, Tokyo, Japan) with the specular component excluded (SCE) geometries. The illuminating and viewing configuration was CIE diffuse/8° geometry. The total color difference (ΔE*ab) represents the sum of all color coordinate differences: L (lightness), a (-a green, +a red) and b (-b blue, +b yellow), and it was calculated as follows: ΔE* = [(ΔL*)2 + (Δa*)2 + (Δb*)2]1/2.
Differences of the Ra values and E values among various composite resins were analyzed statistically by one-way analysis of variance (ANOVA) and a Scheffe multiple comparison test (p = 0.05). Also, (1) difference of the Ra values between before and after polishing, (2) the ΔE values for differences between after polishing and after staining were analyzed statistically by Student t-test (p = 0.05).
III. RESULTS
The results of the Ra values according to the type of composite resin and polishing are shown in Table 2.
The Ra values after polishing were decreased significantly in all type of resins (p < 0.05).
The Ra values of nanofilled and hybrid composite resin were lower than microfilled and flowable resin before polishing (p < 0.05). No significant difference was found between nanofilled and hybrid composite resin, between microfilled and flowable composite resin before polishing (p > 0.05).
After polishing, the flowable composite resin showed the smoothest surface, followed by the nanofilled, the hybrid, and the microfilled composite resins. But, there was no significant difference between flowable and nanofilled composite resin, between nanofilled and hybrid composite resin, and between hybrid and microfilled composite resin (p > 0.05).
ΔE values by the measuring SCE geometry after polishing and after staining are shown in the Table 3.
ΔE values between after polishing and after staining were not different in hybrid and microfilled composite resin (p > 0.05). After staining, ΔE value of nanofilled composite resin decreased significantly, ΔE value of flowable composite resin increased rather (p < 0.05).
ΔE values among all type of composite resins after polishing were not significantly different (p > 0.05).
After staining, ΔE value of flowable composite resin was the highest and different from others (p < 0.05).
IV. DISCUSSION
High quality finishing and polishing can improve the aesthetics and longevity of direct tooth-colored restorations32). The presence of surface irregularities arising from poor finishing and polishing may create clinical problems such as staining, plaque retention, gingival irritation, and recurrent caries2,33,34). However, it is difficult to finish and polish the composite resin restorations to the completely smooth surface. In the present study, the Ra values after polishing were decreased significantly in all type of resins (p < 0.05). Therefore, proper finishing and polishing of composite resin restorations are important steps in restorative dentistry6).
Surface micromorphology of resin composites after polishing has been shown to be influenced by the size, hardness and amount of filler particles in composite35). In several studies1,16), it was also reported that larger filler-particle size resulted in greater Ra values. And, an increase in the amount of filler content results in smoother surfaces because of decreased particle size and better distribution within the resin matrix9). Sarac et al.17) reported that the lowest value was obtained with nanohybrid composite resin in nanohybrid, microhybrid, and hybrid composite resins. And, the highest Ra was obtained with hybrid resin. But, previous other studies1,36) have shown that no significant difference was found among various types of composite resins. In this study, the order of surface roughness from the roughest to the smoothest after polishing was microfilled, followed by the hybrid, then the nanofilled, and finally with the flowable composite resin. The Ra of nanofilled composite resin is similar to the Ra of flowable resin. The reason of this result is assumed that filler size of nanofilled resin is the smallest and filler volume percentage is the highest than others, so it polished more uniformly. But, total filler volume percentage of flowable resin was the lowest than others, and resin matrix contents were higher than others. Extremely increased matrix contents seemed to make smooth surfaces after polishing.
The surface conditions of resin composite restorations change during finishing and polishing procedures. The specular component is the reflected light from the surface such that the angle of reflection equals the angle of incidence. Inclusion or exclusion of a specular component may influence the measured color of composites with different surface conditions. The SCI geometry includes the specular component of the reflected light by placing a white cap at the specular reflection point in the integrating sphere. The SCE geometry excludes the specular component of the reflection by opening the white cap31).
An increasingly roughed surface will reflect the individual segment of specular beam at slightly different angles. Lee et al.31) stated that the SCE measuring geometry is more appropriate to detect small color differences of dental esthetic restorative materials when the surface conditions are not the same. Therefore, in this study SCE geometry was employed to measure the color of dental restorative materials.
Dietschi and colleagues37) showed that (1) the staining may be related to a high resin content and water adsorption; (2) the resin matrix, which is a major component of composite resins, has been reported to be critical in color stability; (3) the higher filler content, the higher color stability.
In this study, when compared after polishing with after staining, ΔE value of nanofilled composite resin decreased significantly. ΔE value of flowable composite resin increased in spite of low Ra value. As, filler contents of flowable resin were lower than other resins, resin matrix contents increased. Therefore, it was seemed that absorption of stains increased.
Staining susceptibility of composites is not related to surface roughness alone, it is related to the volume and size of fillers. Increased filler size and filler content resulted in decrease of organic matrix. So, the amounts of color change were lower1).
In this study, ΔE value of flowable composite resin was the highest after staining and different from others. In spite of the difference of size and volume of fillers among the used resins except flowable resin, color stability was not different statistically. But, in case of flowable resin due to extremely lower filler content, color stability was lower than others. In vitrosurface roughness and staining test, these results proved that the staining susceptibility of composites is not related to extrinsic factors such as surface roughness alone, but to intrinsic factors such as filler and especially matrix composition as well.
A ΔE value of 3.7 or less is considered to be clinically acceptable according to Johnston and Kao38). In this study, after staining ΔE value of nanofilled, hybrid, microfilled composite resin was lower than 3.7, it's result was acceptable clinically. In anterior restoration, the use of nanofilled, hybrid, and microfilled composite resins would be acceptable when considered color stability. But, after staining ΔE value of flowable composite resin was higher than 3.7, color stability was very low. Therefore, though surface smoothness of flowable resin was good, flowable resin was unfavorable in color stability.
Compared with others, nanofilled composite resin wasn't excellent in surface roughness and color stability. And, further research is needed to assess the surface roughness and the color stability of other nanocomposites.
V. CONCLUSIONS
The Ra after polishing was decreased regardless of type of composite resins (p < 0.05).
After resin showed the smoothest surface, followed by the nanofilled, the hybrid, and the microfilled composite resins. But, there were no significant differences between flowable and nanofilled composite resin, between nanofilled and hybrid composite resin, and between hybrid and microfilled composite resin (p > 0.05).
ΔE values among all type of composite resins after polishing were not significantly different (p > 0.05). After staining, ΔE value of flowable composite resin was the highest and different with others (p < 0.05).
Within the limitations of this study, nanofilled composite resin, except the flowable resin, was not different with other composite resins in surface roughness after polishing and color stability after staining.
- 1. Paravina RD, Roeder L, Lu H, Vogel K, Powers JM. Effect of finishing and polishing procedures on surface roughness, gloss and color of resin-based composites. Am J Dent. 2004;17: 262-266.PubMed
- 2. Yap AU, Yap SH, Teo CK, Ng JJ. Finishing/Polishing of composite and compomer Restoratives:Effectiveness of One-step Systems. Oper Dent. 2004;29: 275-279.PubMed
- 3. Bollen CML, Lambrechts P, Quirynen M. Comparison of surface roughness of oral hard materials to the threshold surface roughness for bacterial plaque retention: a review of the literature. Dent Mater. 1997;13: 258-269.ArticlePubMed
- 4. Chan KC, Fuller JL, Hormati AA. The ability of foods to stain two composite resins. J Prosthet Dent. 1980;43: 542-545.ArticlePubMed
- 5. Cho KJ, Park SJ, Cho HG, Kim DJ, Hwang YC, Oh WM, Hwang IN. Influence of the surface roughness on translucency and surface color of the dental composite resins. J Korean Acad Conserv Dent. 2006;31: 312-322.
- 6. Roeder LB, Powers JM. Surface roughness of resin composite prepared by single-use and multi-use diamonds. Am J Dent. 2004;17: 109-112.PubMed
- 7. Pratten D, Johnson G. An evaluation of finishing instruments for an anterior and posterior composite resin. J Prosthet Dent. 1988;60: 154-158.PubMed
- 8. Strassler HE. Polishing composite resins. J Esthet Dent. 1992;4: 177-179.PubMed
- 9. Reis AF, Giannini M, Lovadino JR, dos Santos Dias CT. The effect of six polishing systems on the surface roughness of two packable resin-based composites. Am J Dent. 2002;15: 193-197.PubMed
- 10. Leinfelder KF. Posterior composite resins: The materials and their clinical performance. J Am Dent Assoc. 1995;126: 663-676.ArticlePubMed
- 11. Willems G, Lambrechts P, Lesaffre E, et al. Three-year follow-up of five posterior composites: In vivo wear results. J Dent. 1993;21: 79-86.PubMed
- 12. Lambrechts P, Braem M, Vanherle G. Evaluation of clinical performance for posterior composite resins and dentin adhesives. Oper Dent. 1987;12: 53-78.PubMed
- 13. Wendt SL, Leinfelder KF. Clinical evaluation of a posterior composite resin: 3-year results. Am J Dent. 1994;7: 207-211.PubMed
- 14. Bayne SC, Heyman HO, Swift EJ Jr. Update on dental composite restorations. J Am Dent Assoc. 1994;125: 687-701.ArticlePubMed
- 15. Venhoven BAM, Gee AJ, Werner A, Davidson CL. Influence of filler parameters on the mechanical coherence of dental restorative resin composites. Biomaterials. 1996;17: 735-740.ArticlePubMed
- 16. Ozgunaltay G, Yazici AR, Gorucu J. Effect of finishing and polishing procedures on the surface roughness of new tooth-coloured restoratives. J Oral Rehabil. 2003;30: 218-224.ArticlePubMedPDF
- 17. Sarac D, Sarac YS, Kulunk S, Ural C, Kulunk T. The effect of polishing techniques on the surface roughness and color change of composite resins. J Prosthet Dent. 2006;96: 33-40.PubMed
- 18. Silikas N, Kavvadia K, Eliades G, Watts D. Surface characterization of modern resin composites: A multitechnique approach. Am J Dent. 2005;18: 95-100.PubMed
- 19. Mitra SB, Wu D, Holmes BN. An application of nanotechnology in advanced dental materials. J Am Dent Assoc. 2003;134: 1382-1390.ArticlePubMed
- 20. Reis AF, Giannini M, Lovadino JR, Ambrosano GM. Effects of various finishing systems on the surface roughness and staining susceptability of packable composite resins. Dent Mater. 2003;19: 12-18.PubMed
- 21. Satou N, Khan AM, Matsumae I, Satou J, Shintani H. In vitro color change of composite-based resins. Dent Mater. 1989;5: 384-387.ArticlePubMed
- 22. Um CM, Ruyter IE. Staining of resin-based veneering materials with coffee and tea. Quintessence Int. 1991;22: 377-386.PubMed
- 23. Chan KC, Fuller JL, Hormati AA. The ability of foods to stain two composite resins. J Prosthet Dent. 1980;43: 542-545.ArticlePubMed
- 24. Fruits TJ, Duncanson MG, Miranda FJ. In vitro weathering of selected direct esthetic restorative materials. Quintessence Int. 1997;28: 409-414.PubMed
- 25. Luce MS, Campbell CE. Stain potential of four microfilled composites. J Prosthet Dent. 1988;60: 151-154.ArticlePubMed
- 26. Powers JM, Fan PL, Raptis CN. Color stability of new composite restorative materials under accelerated aging. J Dent Res. 1980;59: 2071-2074.ArticlePubMedPDF
- 27. Stober T, Glide H, Lenz P. Color stability of highly filled composite resin materials for facings. Dent Mater. 2001;17: 87-94.ArticlePubMed
- 28. Barkmeier WW, Cooley RL. Evaluation of surface finish of microfilled resins. J Esthet Dent. 1989;1: 139-143.ArticlePubMed
- 29. Douglas RD, Brewer JD. Variability of porcelain color reproduction by commercial laboratories. J Prosthet Dent. 2003;90: 339-346.ArticlePubMed
- 30. O'Brien WJ, Boenke KM, Groh CL. Coverage errors of two shade guides. Int J Prosthodont. 1991;4: 45-50.PubMed
- 31. Lee YK, Lim BS, Kim CW. Effect of surface conditions on the color of dental resin composites. J Biomed Mater Res. 2002;63: 657-663.ArticlePubMed
- 32. Weitman RT, Eames WB. Plaque accumulation on composite surfaces after various finishing procedures. J Am Dent Assoc. 1975;91: 101-106.ArticlePubMed
- 33. Dunkin RT, Chambers DW. Gingival response to class V composite resin restorations. J Am Dent Assoc. 1983;106: 482-484.ArticlePubMed
- 34. Yap AU, Mok BY. Surface finish of a new hybrid aesthetic restorative material. Oper Dent. 2002;27: 161-166.PubMed
- 35. Choi MS, Lee YK, Lim BS, Rhee SH, Yang HC. Changes in surface characteristics of dental resin composites after polishing. J Mater Sci Mater Med. 2005;16: 347-353.ArticlePubMedPDF
- 36. Uctasli MB, Bala O, Gull A. Surface roughness of flowable and packable composite resin materials after finishing with abrasive discs. J Oral Rehabil. 2004;31: 1197-1202.ArticlePubMed
- 37. Dietschi D, Campanile G, Holz J, Meyer JM. Comparison of the color stability of ten new-generation composites: an in vitro study. Dent Mater. 1994;10: 353-362.ArticlePubMed
- 38. Johnston WM, Kao EC. Assessments of appearance match by visual observation and clinical colorimetry. J Dent Res. 1989;68: 819-822.ArticlePubMedPDF
REFERENCES
Tables & Figures
REFERENCES
Citations
Citations to this article as recorded by 
- Effect of contemporary polishing systems on hardness and roughness of one-shaded dental composites
Kivanc Dulger, Gencaga Purcek
Journal of the Australian Ceramic Society.2025; 61(3): 841. CrossRef - Physicomechanical properties and polymerization shrinkage of the newly developed radiopaque flowable composite derived from rice husk
Nor Ain Fatihah Azlisham, Yanti Johari, Dasmawati Mohamad, Mohd Firdaus Yhaya, Zuliani Mahmood
Polymer Composites.2025; 46(7): 5924. CrossRef - Highly Filled Flowable Composite Resins as Sole Restorative Materials: A Systematic Review
Konstantinos Tzimas, Eftychia Pappa, Maria Fostiropoulou, Efstratios Papazoglou, Christos Rahiotis
Materials.2025; 18(14): 3370. CrossRef - Effect of immersion and thermocycling in different beverages on the surface roughness of single- and multi-shade resin composites
Aiah A. El-Rashidy, Omar Shaalan, Rasha M. Abdelraouf, Nour A. Habib
BMC Oral Health.2023;[Epub] CrossRef - Degree of conversion and physicomechanical properties of newly developed flowable composite derived from rice husk using urethane dimethacrylate monomer
Nor Ain Fatihah Azlisham, Yanti Johari, Dasmawati Mohamad, Mohd Firdaus Yhaya, Zuliani Mahmood
Proceedings of the Institution of Mechanical Engineers, Part H: Journal of Engineering in Medicine.2023; 237(12): 1339. CrossRef - Translucency and Color Stability of a Simplified Shade Nanohybrid Composite after Ultrasonic Scaling and Air-Powder Polishing
Ksenia Babina, Maria Polyakova, Inna Sokhova, Vladlena Doroshina, Alexandr Zaytsev, Elena E. Nikonova, Gleb S. Budylin, Evgeny A. Shirshin, Christian Tantardini, Nina Novozhilova
Nanomaterials.2022; 12(24): 4465. CrossRef - Surface properties and color stability of dental flowable composites influenced by simulated toothbrushing
Guangyun LAI, Liya ZHAO, Jun WANG, Karl-Heinz KUNZELMANN
Dental Materials Journal.2018; 37(5): 717. CrossRef - Topography and surface roughness of fluid resins used as bioprotectors of mini-implants
Rogério Lacerda-Santos, Mirella de Fátima Liberato de Moura, Fabíola Galbiatti Carvalho, Hugo Lemes Carlo, Matheus Melo Pithon, Bruno Alessandro Silva Guedes de Lima, Tibério Andrade dos Passos
Applied Adhesion Science.2014;[Epub] CrossRef
ePub Link
Cite
XML DownloadSurface roughness and color stability of various composite resins
Surface roughness and color stability of various composite resins
Composite resins used in this study
Ra values before and after polishing (Mean ± SD)
abc: Different letter indicates significant differences between the groups in vertical row (p < 0.05).
Measured color (ΔE) after polishing and staining with SCE geometry (Mean ± SD)
ab: Different letter indicates significant differences between the groups in vertical row (p < 0.05).
Table 1
Composite resins used in this study
Table 2
Ra values before and after polishing (Mean ± SD)
abc: Different letter indicates significant differences between the groups in vertical row (
Table 3
Measured color (ΔE) after polishing and staining with SCE geometry (Mean ± SD)
ab: Different letter indicates significant differences between the groups in vertical row (